Klubertop TP 46-111

Technical data sheet of Klubertop TP 46-111

Article number

099173

Low serving temperature

-40 °C / -40 °F

High serving temperature

180 °C / 356 °F

Color

Black

Density, DIN EN ISO 2811, at 20 °C approx.

1.18 g/cm³

Cross adhesion, PA-063 based on DIN EN ISO 2409

0 Gt

Klüber pin-disc tester for testing the service life of bonded coatings, temperature: 25 °C, load: 20 N, speed: 10 m/min, sliding contact: point, sliding distance

1,152 m

Klüber pin-disc tester for testing the service life of bonded coatings, temperature: 25 °C, load: 20 N, speed: 10 m/min, sliding contact: point, coefficient of friction (µ)

0.10

Coefficient of friction, Tannert slip index, room temperature, vmax = 0.243 mm/s, F = 300 N

0.06

Stick-slip, Tannert slip index, room temperature, vmax = 0.243 mm/s, F = 300 N, rated

No jamming phenomenon

Media resistance of the coating, based on DIN EN ISO 2812-1, tested at room temperature, layer thickness approximately 15 µm, base material steel, media soda ash, result: media resistant film, tested up to

400 hours

Media resistance of the coating, based on DIN EN ISO 2812-1, tested at room temperature, layer thickness approximately 15 µm, material ST 1303 steel, media diester oil, result: media resistant film, tested to

500 hours

Media resistance of the coating, based on DIN EN ISO 2812-1, tested at room temperature, layer thickness approximately 15 µm, material ST 1303 steel, media blended with mineral oil, result: media resistant film, tested to

500 hours

Vehicle resistance of the coating, based on DIN EN ISO 2812-1, tested at room temperature, layer thickness approximately 15 µm, base material steel, vehicle 0.1n hydrochloric acid, result: vehicle resistant film, tested up to 400 hours

400 hours

Salt spray test, DIN EN ISO 9227, related to DIN EN ISO 7253, 5% NaCl, temperature 35°C, material is galvanized-phosphatized steel, layer thickness 15 µm, post-corrosion

> 400 hours

Performance with tribo-film thickness 10 micrometers approx.

31 m²/l

Minimum shelf life from date of manufacture – in a dry place, protected from freezing and in unopened original packaging, approx.

12 months

Key features of Klubertop TP 46-111

Klubertop TP 46-111 creates a dry surface, effectively reducing friction and wear, and improving lubrication performance in industrial applications.

Klubertop TP 46-111 resists wear throughout its life, especially when exposed to low to medium loads, and adheres strongly to surfaces, protecting parts from wear.

Unlike conventional lubricants, Klubertop TP 46-111 does not pose a risk of contamination, making it ideal for applications requiring high hygiene standards and avoiding grease contamination.

With its thin yet effective coating, Klubertop TP 46-111 saves costs and optimizes space in the production process, especially useful when coating small parts or series.

Klubertop TP 46-111 has excellent adhesion to many metals and plastics, allowing for a wide range of applications in various industries. Klubertop TP 46-111 is resistant to oils and chemicals, helping to protect components in harsh working environments and chemical attacks.

With its ability to reduce friction and wear, Klubertop TP 46-111 helps extend the life of components while optimizing performance throughout use.

Application of Klubertop TP 46-111

Klubertop TP 46-111 is used to lubricate and protect moving parts such as bearings, shafts in engines and gearboxes. Klubertop TP 46-111 helps reduce friction, protects bearing parts from wear and corrosion, prolonging the life of machine parts.

Klubertop TP 46-111 protects critical components such as slideways, bearings and other small parts, helping to ensure consistent performance and protect components from damage due to friction and corrosion.

Klubertop TP 46-111 lubricates and protects moving parts in food production line machinery, while protecting surfaces from corrosion, ensuring optimal performance and long equipment life.

Klubertop TP 46-111 provides protection for sliding and bearing components in the harsh working environments of the oil and gas industry, where there is contact with lubricants and corrosive substances.

Klubertop TP 46-111 is used in automation systems, including robots and automated machines, to reduce friction, protect moving parts and increase operating efficiency.

In metalworking, Klubertop TP 46-111 protects cutting tools and machinery from wear and corrosion, helping to increase the durability and efficiency of equipment during production.

Klubertop TP 46-111 is used in pharmaceutical production equipment, helping to protect and lubricate machine parts, ensuring the production process runs smoothly without affecting product quality.

Klubertop TP 46-111 supports the maintenance and protection of machine components in production systems, helping to extend equipment life and ensure stable operation during maintenance procedures.