Klubertop TG 05 N

Technical data sheet of Klubertop TG 05 N

Article number

099204

Minimum operating temperature

-40 °C / -40 °F

Maximum operating temperature

300 °C / 572 °F

Color

Grey

Density, DIN EN ISO 2811, at 20 °C

About 1.07 g/cm³

Performance with 10 micrometer tribo-film thickness

About 15 m²/l

Circular bending test (folding machine test), DIN EN ISO 1519, material steel, layer thickness 15 µm, temperature -40 °C, folding mandrel diameter 2 mm, result

Obtain

Cross adhesion (test bar), PA-063 based on DIN EN ISO 2409, value 0 Gt

Circular bend test (folding machine test), DIN EN ISO 1519, material steel, layer thickness 15 µm, room temperature, folding mandrel diameter 2 mm, result

Obtain

AC²T ball/disc sliding friction tester, ambient temperature, v = 0.16 m/s, F = 10 N, layer thickness 15 µm, sliding distance

>= 1 150 m

Coefficient of friction, Tannert slide tool, room temperature, vmax = 0.243 mm/s, F = 50 - 300 N

0.08

Stick-slip, Tannert slide tool, room temperature, vmax = 0.243 mm/s, F = 50 - 300 N, rated

No stick-slip

Abrasion resistance of the coating, based on DIN EN ISO 2812-1, test at room temperature, layer thickness approx. 15 µm, material steel, caustic bleach, results

Film resistant, tested up to 1,000 hours

Abrasion resistance of the coating, based on DIN EN ISO 2812-1, test at room temperature, layer thickness approximately 15 µm, steel material, hydrochloric acid 0.1n, results

Film resistant, tested up to 1,000 hours

Abrasion resistance of the coating, based on DIN EN ISO 2812-1, tested at room temperature, layer thickness approximately 15 µm, material steel, diester oil, results

Film resistant, tested up to 1,000 hours

Abrasion resistance of the coating, based on DIN EN ISO 2812-1, tested at room temperature, layer thickness approx. 15 µm, material steel, mineral oil, results

Film resistant, tested up to 1,000 hours

Salt spray test, DIN EN ISO 9227, in accordance with DIN EN ISO 7253, 5% NaCl, temperature 35°C, material zinc-phosphate steel, layer thickness 15 µm, post-corrosion

>= 36 hours

Salt spray test, DIN EN ISO 9227, 5% NaCl, in accordance with DIN EN ISO 7253, temperature 35°C, reinforced steel, layer thickness 15 µm, post-corrosion

>= 24 hours

Minimum shelf life from date of manufacture - in a dry, non-frozen place and in unopened original packaging, approx.

24 months

Key features of Klubertop TG 05 N

Klubertop TG 05 N provides powerful protection against aggressive agents such as oils and chemicals, effectively protecting phosphate surfaces from corrosion and damage caused by environmental influences.

Klubertop TG 05 N has the ability to operate stably over a wide temperature range, from low to high temperatures, helping to maintain optimal performance under severe operating conditions.

Klubertop TG 05 N is not only effective in dry conditions, but can also lubricate effectively in wet environments, ensuring the stability and long-term performance of machine parts.

Klubertop TG 05 N is specially designed for use in applications where lubrication is required to reduce friction and wear, thereby extending the life of mechanical components.

Klubertop TG 05 N has outstanding anti-wear properties, which help to minimize wear on components and optimize work efficiency throughout the service life.

With good resistance to oil and chemicals, Klubertop TG 05 N helps protect surfaces from adverse environmental impacts, providing peace of mind for users.

Klubertop TG 05 N has a low coefficient of friction, which helps reduce friction during operation, thereby optimizing work performance and saving energy.

Application of Klubertop TG 05 N

Klubertop TG 05 N is ideal for automotive engine components, such as pistons and other parts subject to wear and friction. Klubertop TG 05 N helps to increase performance and prolong the service life of engine components.

In the field of manufacturing precision parts, such as bearings, precision machining and other mechanical devices, Klubertop TG 05 N provides excellent lubrication, which helps to minimize friction and wear, while improving the efficiency and durability of the parts.

Klubertop TG 05 N is used in textile and sewing machine components where friction reduction and consistent performance are required throughout the production process. Klubertop TG 05 N can also be applied to wear components in fabric processing, helping to reduce wear and protect equipment.

In electrical applications, especially with motors and electromechanical components, Klubertop TG 05 N helps protect components against wear and friction, while optimizing operating performance and reducing maintenance costs.

Klubertop TG 05 N is resistant to high temperatures and harsh environmental conditions, making it the ideal choice for applications requiring long-term stability and high reliability, from heavy industry to systems operating under harsh conditions.